Progress has been made in the study of calcium fluoride crystal defects by the Chinese Academy of Sciences. Calcium fluoride crystals feature a wide transmission wavelength range, low dispersion effects, and strong resistance to laser damage, making them core components in advanced instruments such as ultraviolet lithography systems, high-resolution space cameras, and high-precision optical detection Peralatan . Namun, struktur kubik terbuka kalsium fluorida menyisakan setengah dari situs kisi oktahedral yang kosong, menghasilkan kepadatan dislokasi 10⁵/cm², yang secara signifikan merusak kinerja. karena itu secara mengidentifikasi, menganalisis, dan mengendalikan dislokasi-DISLOKASI-LAGI-KONSTITICE di dalamnya, CRYCTICE-LAGI KRISTUTIONAL ADALAH ADALAH ADALAH ADALAH ADALAH ADALAH ADALAH, ANALISIS, DAN PENGENDALIAN DISLOKASI-KONSTITIONAL DALAM KONSTITICE DALAM POINECHOUGH TERSEDIA DENGAN EREADTHOUGH TERTIK kristal fluoride dan memenuhi persyaratan aplikasi ekstrem . karena sensitivitas f-ion terhadap balok elektron, karakterisasi tingkat atom dari dislokasi dalam kristal kalsium fluoride telah menimbulkan tantangan yang signifikan, dan teknik karakterisasi tradisional telah berjuang untuk menyelesaikan dan mengklarifikasi konfigurasi dislokasi mereka dan mekanisme formasi {mekanisme formasi {{Formasi {{{{{{{{{{{{{mekanisme pembentukan {{Formasi {{Formasi {Formasi {
In response, a research team led by Dr. Liangbi Su and Dr. Bo Zhang from the Shanghai Institute of Ceramics, Chinese Academy of Sciences, addressed the technical bottlenecks in atomic-level characterization of dislocations in calcium fluoride crystals. They developed a multi-scale integrated characterization system combining "chemical etching method-high-resolution electron backscatter diffraction (HR-EBSD)-integrated differential phase contrast scanning transmission electron microscopy (iDPC-STEM)." The study developed a high-resolution EBSD technique based on the Kikuchi line rotation compensation algorithm, overcoming the limitations of traditional EBSD precision, and combined it with chemical etching to achieve precise localization and Karakterisasi perbedaan orientasi kecil untuk dua jenis dislokasi dalam kristal: "terdistribusi bebas" dan "secara teratur teragregasi ." Selain itu, penelitian ini menggunakan oM-dosis-dosis-dosis-stem {oomasi {oomasi f/ca {skala atom pada waktu pertama dan dengan jelas memangkas sekelompok sejati.
Analisis perbedaan morfologi, distribusi, dan orientasi dislokasi dalam kristal kalsium fluoride
Furthermore, by integrating crystal growth experiments, first-principles calculations, and structural characterization, the researchers elucidated the mechanism of dislocation formation in calcium fluoride crystals. The study found that excessive temperature gradients cause lattice mismatch, thereby promoting dislocation formation. Additionally, the study clarified the causal relationship between vacancy-preferred aggregation and Frank Nukleasi dislokasi yang tidak lengkap pada skala atom . berdasarkan temuan ini, penelitian ini mengusulkan strategi untuk menekan/mengurangi cacat dislokasi dan memvalidasi kemungkinan "dislokasi mandiri" melalui level yang dikurangi. cm⁻ cm. Mencapai kristal kalsium fluorida yang tidak cacat .
Studi ini membahas tantangan ilmiah yang sudah lama ada untuk mencapai "resolusi tingkat atom" cacat dalam kristal kalsium fluoride dan menetapkan rantai kognitif lengkap dari makroskopik ke tingkat cacat mesoscopic dan atom {4} {4} {4} {4} {4.